Effect of Moisture Content of Green Sand on The Casting Defects
DOI:
https://doi.org/10.37385/jaets.v2i1.77Keywords:
sand casting, green sand, moisture content, Al-Si, casting defectsAbstract
In this study, three percentages of moisture content on the green sand were benchmarked to be observed their effects on the casting defects. The metal used is scrap Al-Si with wt% of Al 59.7. The metal was melted in a furnace at 550 ºC then poured into sand molds and cooled for 24 hours before it can be removed, cleaned, and finished. There were prepared three specimens for each benchmark. Qualitative observation of defects was done by physical observations on the surface of the specimens. The observations show that on the moisture content of 2.5%, there is a defect in the form of porosity. Defects in the form of drops, misruns, blowholes, and shrinkage cavity are found on the benchmark 3.5%. The most severe defects are found on the benchmark 4.5% in the form of buckles and severe shrinkage cavities that are found in almost all specimens.
Downloads
References
Astika, I. M., Negara, D. P., & Susantika, M. A. (2010). Pengaruh Jenis Pasir Cetak dengan Zat Pengikat Bentonit terhadap Sifat Permeabilitas dan kekuatan Tekan Basah Cetakan Pasir (Sand Casting). Jurnal Energi Dan Manufaktur.
Chastain, S. (2004). Metal Casting: A Sand Casting Manual for the Small Foundry.
De Garmo, E. P., Black, J., & Kohser, R. (2003). Materials and processes in manufacturing, Hoboken. In: NJ: Wiley.
Desiana, S. (2012). Pengaruh Variasi Waterglass Terhadap Kadar Air Dan Kadar Lempung Pada Pasir Cetak.
Hendronursito, Y., & Prayanda, Y. (2016). Potensi Pasir Lokal Tanjung Bintang Pada Aluminium Sand Casting Terhadap Porositas Produk Hasil Cor Aluminium. Jurnal Kajian Teknik Mesin, 1(2), 60-68.
Jatimurti, W., Alexander, B., & Toto Wibisono, A. (2019). Effect of Degassing Time and Cooling Rate on Microstructure and Porosity of Aluminum 6061 Alloy Using Sand Casting Method. Paper presented at the Materials Science Forum.
Kaushish, J. P. (2010). Manufacturing Processes.: PHI Learning.
Sama, S. R., & Manogharan, G. (2017). Sand casting design rules: Pennsylvania State Univesrity.
Sharma, P. C. (2007). Production Technology (Manufacturing Processes): Manufacturing Processes: S. Chand.
Siagian, S. J., Gede, I., Istri, C., & Dan Kusuma, P. J. J. I. T. D. M. (2017). Pengaruh Permeabilitas Cetakan Pasir Dan Penambahan Silikon (Si) Pada Proses Pengecoran Terhadap Kekerasan, Porositas Dan Struktur Mikro Alumunium Silikon (Al-Si). 6(4), 305-310.
Surdia, T., & Chijiwa, K. (2006). Teknologi Pengecoran Logam Cetakan ke sembilan. Jakarta: Pradnya Paramita.
Taryaman, T., Roslina, R., & Abdullah, H. (2018). Analisis Cacat Cor pada Produk Fly Wheel Hasil Proses Pengecoran Menggunakan Cetakan Pasir. Metal Indonesia, 27(1), 44-55.
Vaishnav, A., & Patel, V. (2016). Reduce Shrinkage-Porosity Defects in Sand Casting Using FEM.
CITEDNESS IN SCOPUS
CITEDNESS IN WOS